We are founded in 1999, Plan Paint products include a variety of paints, finishes, coatings, applicators, and varnishes sold under the names Plan Paint, Aeon, Best, Diamond, Daltron, Dmaxox and Maxox and make to order, It selis Paints for industrial use such as on plastics, metal, glass, fiberglass, automotive finishing and refinishing products.
Chemical name : Poly Acrylate Resin Solution combined with Cellulose Acetate Butyrate Resin.
Description for use : High quality 2K Acrylic Base Coat Binder suitable for metallic, pearl effects and solid color in 2K clear on base of 2K automotive refinish system for passenger cars, commercial vehicles and buses.
It easy application, extremely metallic and pearl orientation, offers brightness effect,hiding power, cloudless, good adhesion inter coats and weathering resistance for top quality 2K automotive refnish system.
Application :
Mixing Ratio: 2K Base Coat color + 2K Thinner 1-2-3 (normal evaporated)
:100 + 80 to 100 by volume
Spray viscosity : approx. 15-18 Sec./ Din cup # 4 / 25 *C
Nozzle : Gravity feed 1.3-1.4 mm.
: Suction feed 1.5-1.7 mm.
Spray pressure : 3-4 bar / 45-60 psi.
Spray applied : 2-3 medium coats , allow 5-10 min. flash off time
between coats
Dry film thickness : approx. 15-25 um in 2-3 coats
Top Clear Coating : after 15 - 20 min. flash off ime, recoated with 2K Clear Coat 2:1/4:1
: 2 - 3 coats ; it becomes high gloss and weathering resistance metallic clear on base finish system.
Chemical Name : Unsaturated Polyester Resins
Description for use : It is a thixotropic polyester putty made from special unsaturated polyester resins, pigments and fine extender, well suitable for medium filling on damage areas.
It is easy to applied, offers good adhesion and stability on vertical surface; easy sanding and smooth surface.
Substrates
1. sanded bare steel without grease and dirty matter
2. sanded old paint work
3. full cured putties and primer or surfacer
Special hint : not suitable for applying on acid cured primer or surfacer
: stirred thoroughly before use and keep close after used.
Application: Apply by putty knife
Mixing Ratio: 2-3% by weight of 2K Premiumn Grade PE Putty Hardener
Gel Time: 5 - 7 min. at 30c
Curing Time: 40 -50 min. / 30*c
Packing: 2kg. / can (gross weight) with hardener 40 g. in PE, tube
Shelf Life:approx. 5 months in original sealed can
Chemical Name : Unsaturated Polyester Resins Mixed with Pigments and Extenders
Description for use : It is a thixotropic polyester putty made from special unsaturated polyester resins, pigments and fine extender,well suitable for thin filling on damage areas. It is easy to applied, offers good adhesion, flexibility and easy sanding.
Substrates
1. sanded bare steel without grease and dirty matter
2. sanded old paint work
3. full cured putties and primer or surfacer
Special hint : not suitable for applying on acid cured primer or surfacer :stirred thoroughly before use and keep close after used
Application : Apply by putty knife
Mixing Ratio : 2-3% by weight of 2K PE Yellow Putty Hardener
Gel Time : 3-5 min, at 30 -35*c
Curing Time : 40-50 min. at 30-35*c
Packing : 4kg. / can (gross weight) with hardener 70 g. in PE. tube
Shelf Life : approx. 5 months in original sealed can
Description : It's medium build / curing two packs epoxy primer coating. It's provides good chemical resistance, especially acids and alkalis, good flexibility and adhesive properties which is mainly used for coating, on passenger car, truck, ship, civil engineering and structural fields.
Out Standing Properties : Excellent fexibility, adhesive strength, impact strength, chemical and water resistance. Excellent anti corrosion. Short time of curing but long pot life of mixing composes. Less toxicity. Can be use as a primer on various
substrate : steel plate, stainless steel, aluminum, zinc or galvanized zinc, fiber glass, concrete etc. Suitable for wet on wet application.
Application
Mixing Ratio : Base (Epoxy) : Hardener : 2K Thinner (normal)
: 1 1 by volume
Special Hints : should be mixed before using 30-60 min.
Pot life after mixed : approx 3 -4 hr.
Spray Viscosity : approx 18 - 22 Sec./ DIN. cup # 4
Nozzle : Gravity feed 1.3 - 1.8 mm, / Suction feed 1.8 - 2.0 mm.
Spray Pressure : 2 -3 bar / 30 -45 psi.
Dry Film Thickness : approx. 80 - 100 มm, at 1 - 2 coats.
Hardness(pencil) : B - HB (overnight)
Touch Free :10 - 15 min.
Putties Applied :after 1.5 - 2 hr. (room temperature)
Hard Dry : over night
Dry Through :after 3-4 days or baking 40 min@ 60*c at metal temperature.
Shelf Life : at least 1 year in original sealed package.
Description for use : It's two packs filler primer based on acrylic polyol resins,designed to satisfy the expectations of the most demanding and qualiied car refinishers. An extremely versatile product suitable for use as a surfacer primer. It can be applied on bare metal,steel plates,stainless steel,zinc, polyester putties,primer and on completely degreased,sanded oniginal fnishes. It's easy application and sanding characteristic.
Application
Mixing ratio = Base : Hardener : 2K Thinner
= 2: 1 : 10-20 % by volume
Pot Life : approx. 1-2 hr. at 30 *C
Reducer : with 10 - 20 % of 2K-Thinner (normal evaporated)
Spray viscosity : approx. 20-25 sec. / Din.cup # 4
Nozzle :Gravity feed 1.3-1.4 mm.
: Suction feed 1.7-1.8 mm.
Spray pressure : 30 -45 psi. / 2-3 bar.
Dry film thickness : approx. 40 -50 micron in 2-3 coats
Flash off time : 5-10 min.
Curing time : 1 hr.-1.5 hr. (sanding) at room temperature
:dry through(overnight) at room temperature
Hardness (pencil) : 2H to 3H (Baking 60 *C@30min.); 2Hafterair
drying over night
Chemical Name : Poly Acrylate Resins Solution Mixed with Pigments and Extenders
Description for use : It's two packs surfacer primer base on high quality of acrylic
polyol resins and pigments and extenders; designed to satisfy the expectation of the
most demanding and qualifed car refinishers. An extremely versatile product suit-
able for use as primer with high filling power or as a sealer with good water and
alkali resistance. It may be applied on bare metal, suitable on polyester putties
primer and on completely dry, degreased, sanded original fnishes.
Easy application and sanding characteristic.
Application
Mixing ratio= Base : Hardener : 2K Thinner
= 2 : 1 : 10-20 % by volume
Pot life : 1-2 hr. / ambient temperature (30 *C)
Spray viscosity : 20 - 25 sec./ Din.cup #4.
Nozzle : Gravity feed 1.3 - 1.4 mm
: Suction feed 1.7 - 2.0 mm
Spray pressure : 3-4 bar / 45-60 psi.
Dry film thickness approx. 50 - 70 micron (2-3 coats), allow 5 - 10 flash off time
Hardness (pencil) : H (overnight) ; 2 H (after 48 hrs.)
Dust free : 5 - 10 min.
Sanding : after 1.5-2 hr.
Dry through : overnight
Baking 40 min @60 C at metl tempure
Company name | PLAN PAINT CO.,LTD | Website URL | https://www.planpaint.com/ |
---|---|---|---|
Street address |
Songkhanong, Samphran Nakhon Pathom Kingdom of Thailand
[See map] |
Person in charge | Earth |
Telephone number | 081-4144919 | Fax number | 0-2489-3376 |
Capital | 3,000,000 THB | Employees | Unregister |
Annual sales | Unregister | EMIDAS Member Number | 102130 |
Main 3 products |
|